: The simulation showed a "mushy zone" that remained liquid far longer than expected. The "Cracked" Moment
: Introduced in version 2021a, this model calculates the hot tearing tendency based on the solidification path. thermocalc cracked hot
Hot tearing is a common casting defect where cracks form at grain boundaries because the remaining liquid cannot fill spaces opened by thermal shrinkage. Guide to Calculating Hot Crack Susceptibility : The simulation showed a "mushy zone" that
: Refer to Example PM_G_07 in the Thermo-Calc Help Menu for a pre-configured hot cracking simulation. thermocalc cracked hot